Ding Xinda and activated carbon manufacturing prices and crushing related questions

Answers
Asked by
Updated
Ding Xinda and activated carbon manufacturing prices and crushing02021-12-03 22:30:23
When the temperature is below 600℃, the specific surface area of carbonized material increases with the increase of temperature.When 600~900℃, the specific surface area reaches a certain value: 250~300 m2/g; when above1000℃, the specific surface area shrinks rapidly. When the carbonization temperature is above 800℃, the reaction performance of carbonized compounds and activation gas gradually becomes weaker, so the carbonization temperature is generally below 1000℃. However, if the residual volatile content and thermal effect are taken into account, the most suitable temperature should be 600~700℃39].gold recovery activated carbon  The carbonized substance obtained from the carbonization process is placed in water vapor or a mixture of water vapor and combustion gas and heat treated at 800~1000℃, which is called the activation process.coconut activated carbon factory   The commonly  sed activation gases are carbon dioxide, water vapor, oxygen, etc., due to the oxidation reaction of these gases on the surface of the carbonized substance, eroding the carbonized substance, thus producing a rich porous structure.(2) Chemical method. Chemical activation method is a method of preparing activated carbon by adding chemicals to the raw materials used or impregnation into the raw materials or carbonized materials, and then heating it at high temperature in inert gas.The chemicals used in chemical activation are generally dehydrating.The more commonly used activator is: inorganic acid varieties have phosphoric acid, sulfuric acid and boric acid, salt varieties have zinc chloride, calcium carbonate and potassium sulfate, alkali varieties have sodium hydroxide, potassium hydroxide, etc. 
Ding Xinda activated carbon distribution sales and crushing02021-12-10 22:21:16
The commonly used activation gases are carbon dioxide, water vapor, oxygen, etc., due to the oxidation reaction of these gases on the surface of the carbonized substance, eroding the carbonized substance, thus producing a rich porous structure.(2) Chemical method.activated carbon for gold recovery  Chemical activation method is a method of preparing activated carbon by adding chemicals to the raw materials used or impregnation into the raw materials or carbonized materials, and then heating it at high temperature in inert gas.The chemicals used in chemical activation are generally dehydrating.The more commonly used activator is: inorganic acid varieties have phosphoric acid, sulfuric acid and boric acid, salt varieties have zinc chloride, calcium carbonate and potassium sulfate, alkali varieties have sodium hydroxide, potassium hydroxide, etc. activated carbon wholesale 
Ding Xinda activated carbon refining manufacturing02022-02-15 22:00:54
1. Combined with Zeta potential, sedimentation experiment, viscosity measurement and other methods, the influence of various dispersants on CEO and slurry suspension effect was studied. The results showed that the formula with good stability was the appropriate concentration of mixed dispersant (NAP +SBN) or (NAP +PAM+SBN).gold recovery from activated carbon  2. The removal rate of CEOZ slurry prepared with mixed dispersant (NAP +PAM+SBN) in the processing of K9 glass by MASJP was higher than that of other mixed dispersants.activated carbon china manufacturers   By comparing the processing effect of MASJP with and without mixed additives, it is found that the processing effect of MASJP with mixed additives (NAP +PAM+SBN) has higher surface quality, which can significantly reduce the interface area between the polished area and the unpolished surface and increase the smooth surface as much as possible.3. Combining online observation and single factor method, the formation process of the surface features of the polished area was studied. The experimental results showed that the surface morphology of the polished area showed a W-shaped bowl structure in the vertical jet machining, and an eccentric bowl structure in the crescent shape in the oblique jet machining.Compared with the abrasive water jet machining effect, it is found that the W shape and crescent shape characteristics of the polishing region of MASJP are relatively flat, the smooth surface is larger and the surface quality is higher. 4. When applying nozzle with different outlet shapes in MASJP, it is found that the fluid ejected from the cylindrical nozzle flows out along the direction of the jet and does not disperse. The processing area of the fan-shaped nozzle is large, the polishing area is approximately a rectangle, and the removal depth near the nozzle is larger.Hollow conical nozzle processing finished parts, the polishing area formed a hollow circle, the central part of the removal of less, the circumference of the removal of deep;The removal depth of the polishing area decreases gradually from the center to the circumference after the finished piece is processed by the solid conical nozzle. 5, the workpiece surface profile and material removal depth with the selection of polishing slurry composition changes.With the increase of abrasive concentration, the material removal depth increases, which is roughly in a proportional relationship.With the increase of abrasive particle size, the material removal depth also increases. 
Ding Xinda activated carbon processing and manufacturing02022-02-10 18:54:54
The polishing slurry and processing technology of micro-abrasive slurry jet were studied.gold recovery from activated carbon  Through the analysis of the physical and chemical properties of additives and their state changes under the jet, the comprehensive effects of the types and proportions of different additives, as well as the types, proportions and particle sizes of abrasive on the formation of uniform slurry, the promotion of good abrasive dispersion and the jet polishing effect were explored.activated carbon china manufacturers   The effects of different types of nozzles, polishing slurry, jet distance, jet time, different initial RA, jet pressure and jet Angle on the surface profile, material removal depth and surface quality of the workpiece were studied through polishing experiments. The local Ra of the optical glass surface is in the range of 20nm~50nm by MASJP, and the lowest Ra is 10.24nm. 1. Combined with Zeta potential, sedimentation experiment, viscosity measurement and other methods, the influence of various dispersants on CEO and slurry suspension effect was studied. The results showed that the formula with good stability was the appropriate concentration of mixed dispersant (NAP +SBN) or (NAP +PAM+SBN). 
Ding Xinda activated carbon anthracite raw materials and prices02022-01-13 22:48:03
Electrochemical modification is to change the electrical and chemical properties of activated carbon surface by using micro electric field, so as to improve the adsorption selectivity and performance.It does not need to add chemical agents, does not need to heat, does not cause pollution to the environment, low energy consumption, only a few hundred millivolts, easy to operate.The results show that the adsorption equilibrium of activated carbon is dependent on the electric potential: the adsorption amount of activated carbon increases with the increase of the potential, and the adsorption speed is accelerated;Arpolarity polarization is beneficial to the adsorption of chloroform by activated carbon, while cathodic polarization inhibits the adsorption of chloroform by activated carbon 3-341]. Activated carbon heteroatom carrier and compound modificationActivated carbon has very high stability and good activity, these two basic properties become the activated carbon as a catalyst or catalyst carrier conditions.By introducing certain heteroatoms and compounds on the surface of activated carbon by liquid phase deposition, the adsorption performance of activated carbon can be increased by using the binding effect between these substances and adsorbents.compounds, which has the advantages of increasing the reaction rate and increasing the adsorption capacity.Yang Quanhong et al. 'Using FESO;Activated carbon material was modified.gold adsorption on activated carbon  The experimental results show that the surface structure of the activated carbon material modified by FeSO changes: the specific surface area decreases, the surface oxygen content increases, the plane of the random layer graphite carbon net is destroyed to a certain extent, and the ammonia absorption capacity and benzene absorption performance of the sample are greatly enhanced.He ChunHong et al. [reported the research progress of supporting activated carbon materials in the removal of SO; the removal ability of SO was significantly enhanced after supporting Co, Ni, Mg, and V compounds, which was due to the formation of Co(OH)2, Ni(OH)2, Mg (OH)2, and V,0 microcrystals on the surface of activated carbon after supporting, which enhanced the desulfurization activity of activated carbon. www.chinactivecarbon.com 
Ding Xinda activated carbon carbon adsorption and carbon principle02021-11-29 22:41:57
② chemical activation method.Activated carbon can be obtained after high temperature treatment by using the gas released by the activator or soaking the raw material with the activator.Activated carbon has a micro product structure, the micro product arrangement is completely irregular, the product body has micropores (radius is less than 20[angstroms]=10-10 meters), through the hole (halfDiameter 20~1000), large hole (radius 1000~100000), so that it has a large inner surface, specific surface area of 500~1700 m 2/ g.This determines that activated carbon has good adsorption, can adsorb the metal ions in waste water and waste gas, harmful gases, organic pollutants, pigments and so on. gold coconut shell activated carbon  Industry should beActivated carbon also requires high mechanical strength, good wear resistance, its structure is stable, small energy required for adsorption, in order to be conducive to regeneration.Activated carbon for oilDecolorization, deodorization, gas separation, solvent recovery and air conditioning of fat, beverage, food and drinking water, used as catalyst or adsorbent for body and gas mask.Physical characteristics:Activated carbon is a kind of multi-aperture carbonization, has a very rich pore structure, has good adsorption characteristics, its adsorption by physical and chemicalAbsorbed from the force, the appearance of the color and lustre is black.Its composition in addition to the main carbon, but also contains a small amount of hydrogen, nitrogen, oxygen, its structure is shaped like a hexagon, due to the irregular hexagon structure, determine the characteristics of its body also incandescentand high surface area, each gram of activated carbon has the equivalent of 1000 square meters than the surface. 
Ding Xinda activated carbon use02021-12-13 00:44:20
2.1.3 Determination of ash content. Put 150mL porcelain cyanosis pot in muffle furnace, burn it at (65020) "℃ to constant weight, put the cyanosis pot in dryer, cool and weigh; Weigh 5 grams of the crushed sample (approximately 0.1mg) and place it in 150mL porcelain coating that has been burned to constant weight; Put Zengtan into a muffle furnace whose temperature does not exceed 300℃, open the cyanosis cap, and gradually increase the temperature to a constant weight at 650 ℃ 20℃. It takes about three hours. Calculate ash value and get ash content.activated carbon for gold recovery  2.1.4 Determination of methylene blue adsorption value. The crushed sample was weighed with 1.0 grams (approximately to 1mg) and placed in a 100mL grinding stopper conical flask. An appropriate amount of methylene blue test solution was added with an eyedrot. The filtrate was placed in a colorimetric dish with a light diameter of LCM, and the absorbance was measured with a spectrophotometer at a wavelength of 665nm. The absorbance was compared with the absorbance of the standard cupric sulfate filter. The number of ml of methylene blue test solution consumed was the methylene blue adsorption value of the sample. activated carbon wholesale  
Ding Xinda activated carbon value02021-12-29 21:32:21
At present, the organic pollution of drinking water source is relatively serious. The organic pollutants themselves are not only highly toxic, but also may generate halogenated disinfection by-products (DBPs) after chlorination disinfection. Meanwhile, the existence of organic compounds will reduce the biological stability of drinking water and lead to the secondary reproduction of microorganisms in the pipe network. Therefore, it is important to reduce the content of organic pollutants in drinking water. Conventional water treatment process has low removal efficiency for organic pollutants, so it is imperative to seek economic and efficient treatment technology. On the basis of giving full play to the advantages of ozone oxidation to remove organic matter, ozone catalytic oxidation technology can induce the formation of highly oxidizing hydroxyl radical (-Oh), which can effectively remove trace organic pollutants that are difficult to degrade in water and reduce the content of ozone oxidation by-products. It is a kind of water treatment method with great prospect.activated carbon for gold recovery  Laboratory studies have shown that ceramic honeycomb activated carbon catalytic ozone oxidation technology and removal of trace organic matter in water has more obvious advantages, but the catalytic oxidation and active carbon process characteristics to be in-depth study, therefore the pilot was investigated through honeycomb ceramic catalytic ozonation and activated carbon catalytic ozonation and activated carbon filter combination process operation characteristics. activated carbon wholesale 
Ding Xinda activated carbon use02021-12-22 00:10:48
High-quality granular activated carbon must have good adsorption performance and strength. Like powdery activated carbon, the adsorption performance of granular activated carbon depends largely on the characteristics of pore structure. The adsorption performance index can be analyzed and characterized by different methods, such as the decolorization performance of activated carbon expressed by methylene blue. Other performance indexes include iodine adsorption value, caramel decolorization rate, etc.activated carbon for gold recovery  The pore structure characteristics and specific surface area of activated carbon are usually obtained by measuring nitrogen adsorption isotherm at low temperature with adsorption apparatus.activated carbon wholesale  For the gas phase adsorption, the size of the gas molecules is usually less than 1. ONM, the use of microporous activated carbon; For liquid-phase decolorization refining, due to the large size of the liquid molecules, it is necessary to use activated carbon with developed mesopore. Activated carbon has a large specific surface area and a particularly developed micro-pore structure, which is the main reason for its strong adsorption capacity and large adsorption capacity. 
Ding Xinda activated carbon block02021-12-22 23:40:43
Activated carbon (AC) is a kind of porous carbon material with developed pore structure and large specific surface area, which is prepared by using biological organic matter (such as wood, coke, petroleum coke, coal and various nut shells, etc.). It is a kind of high quality adsorbent.activated carbon pellets wholesale   With the development of industry, its application is more and more extensive.www.powdered-activated-carbon.com  At present, it has been widely used in the field of environmental protection, food industry and medicine. The granular activated carbon with high strength was prepared by heating wood phosphate mixture at low temperature and using tar generated during its pyrolysis as binder. In this paper, the process conditions and plasticizing mechanism of granular activated carbon prepared by phosphoric acid were studied, which provided scientific data and theoretical basis for the preparation of high strength granular activated carbon. Fir chip as the raw materials, H - POs as activator, using single factor analysis and orthogonal experimental design method, this paper discusses the influence granular activated carbon pore structure and the iodine adsorption value, methylene blue and strength of various preparation factors, determine the optimum process conditions of preparation of granular activated carbon phosphoric acid, phosphoric acid concentration is 70%, dipping 180%, kneading temperature is 170 ℃, for 60 min kneading time, activation temperature is 350 ℃, the activation time of 210 min. The iodine adsorption value, methylene blue adsorption value, strength and BET specific surface area of GAC were 1020.04mGG, 225mg/g, 88.73% and 1486.48m2/g respectively. The experimental results show that the impregnation ratio and carbon activation temperature have great effects on the adsorption performance of GAC, while the kneading temperature and impregnation ratio have great effects on the strength of GAC. Because the strength of GAC decreases with the increase of impregnation ratio, and the decrease range is large, so the preparation of GAC with compound activator is proposed. The results show that the composite activator can reduce the impregnation ratio of phosphoric acid to wood chips and improve the strength of granular activated carbon. At the same time, the composite activator can improve the adsorption performance of GAC. Therefore, granular activated carbon with good adsorption performance and high strength can be prepared by this method. 
Ding Xinda activated carbon use development02021-12-13 00:46:10
Principle of activated carbon adsorption activated carbon is a kind of very small granular has a large surface area, and more tiny holes in the granular - capillary. The capillary has very strong adsorption capacity, due to the granular surface area is large, so a good contact with with gas (impurities). When these gases (impurities) encounter capillary by adsorption, purification effect. Activated carbon surface area of the study is very important, only the BET specific surface area detecting data of active carbon method detected result is reliable, domestic at present there are many instruments can only make direct comparison method of detection,www.powdered-activated-carbon.com  In domestic has been eliminated. Specific surface area test unified the multi-point BET method at home and abroad, specific surface area measurement standards are developed at home and abroad is based on BET test method, please see our national standard (GB/T 19587-2004) - gas adsorption BET principle of solid material specific surface area measurement methods. Specific surface area testing is actually the more time-consuming jobs, as the adsorption capacity of sample is different, some sample testing may need to spend the whole dayTime, if the test process is not fully automated, the tester can not leave at any time, and should be highly focused, observe the dashboard, control the knob, a little careless will lead to the failure of the test process, which will waste a lot of valuable time of the tester.activated carbon pellets wholesale  F - Sorb 2400 specific surface tester is really able to BET method detection instruments (both direct comparison method), the more important F - Sorb 2400 specific surface tester is by far the only specific surface area of the fully automated intelligent testing equipment, the test results with the international high consistency, the stability is very good also, at the same time reduce the human error, improve accuracy test results. 
Ding Xinda activated carbon decomposition02021-12-14 23:34:22
The experimental results show that the adsorption equilibrium of pure components is in good agreement with the Langmuir equation. In the case of multi-component adsorption, due to the competition and interference between each component, the component with strong adsorption ability can replace the other component that has been absorbed, so that the penetration curve of each component has obvious changes. activated carbon for gold recovery  The penetration point of the components with relatively weak adsorption capacity was significantly advanced, while the penetration time of the components with strong adsorption capacity was delayed. In this paper, E-L equation and IAST theory are used for theoretical prediction and analysis of multi-component adsorption equilibrium, and compared with experimental results.activated carbon wholesale   The results show that although the prediction of total adsorption amount by E-L equation is in good agreement with the experimental results, the prediction of each component adsorption amount by E-L equation often produces positive and negative deviation, and the average error is usually more than 20%. However, IAST can eliminate the positive and negative deviation well, and the average error is less than 10%, which is more consistent with the experimental results. The operating parameters showed that the adsorption capacity of activated carbon would decrease with the increase of temperature, gas velocity or humidity. The appropriate operating range is: temperature within 40℃, gas speed between 0.1~0.5 m/s, humidity is best not more than 40%. In this rang 

Ask New Question  

  • You are not logged in,answer will be Anonymous.Set Nickname | Sign In | Sign Up
  • tags separate by ','
  • Shortcuts:Ctrl+Enter

Latest Questions